What Should Be Done If There Are Water Marks And Oxidation When Processing Low-E Glass?

As the weather gets hotter and hotter, a part of the customer washing mill after a winter using and there are water marks and oxidation. What should be done if there are water marks and oxidation when processing Low-E glass?

Suggestions are as follows:

1.The cutting tool head of the cutting machine of sheet glass has a large amount of oil and a lot of oil.The result is that the cleaning is not complete.It is recommended to use special cutting oil and reduce the amount of cutting oil to control its width within the range of flat glass film removal.

2. The water in the water tank of the edge of sheet glass grinding machine is lubricated with many microbes.It is recommended to add 84 disinfectant during maintenance.Run a water cycle to eliminate microorganisms in the water.

3. Adding a photoelectric induction flush pipe at the end of the edge of flat glass grinder, which can help improve the cleaning efficiency of the washer.

4. Cleaning the cleaning section with pure water.And the pure water should be replaced at least 8 hours.Ordinary tap water can be used in the grinding section. It is recommended to use pure water replaced by washing section.

5. After the completion of washing the flat glass film, the part of the sheet glass receiving sheet shall be stowed, and the sheet glass shall be separated by corks.The purpose of this is to further air dry the internal water stains.

6. At the end of the washing section, the sheet glass collector shall wear a mask to prevent the personnel saliva and droplets from flying

7. At the entrance of dryer air box of the cleaning section, non-woven cloth or filter cotton should be covered and replaced regularly.The reason is as follows: the dust in the workshop is large, and it is not brushed for a long time. The speed of the brush is controlled.The Low-E glass washing speed is 2/3 of that of clear glass.

8. Strengthen the safety awareness of personnel. Some operation procedures and labor protection supplies of personnel shall be cleaned or replaced according to the requirement to form a water mark with dust on the sheet glass surface.

9. The brush of the flat glass film washer shall be soft wool.

10. To strengthen the awareness of equipment maintenance, personnel shall regularly maintain and supervise the inspection according to the maintenance plan.